Hoque, S. M. and Hakim, M. A. and Khan, F. A. and Dan, N. H. (2007) Effect of Tb substitution on the magnetic properties of exchange-biased Nd2Fe14B/Fe3B. JOURNAL OF MATERIALS SCIENCE , 42 (22). 9415-9420 . ISSN 0022-2461
Full text is not hosted in this archive but may be available via the Official URL, or by requesting a copy from the corresponding author.
Official URL: http://www.springerlink.com/content/13m64848237444...
Abstract
Tb-substituted (Nd,Tb)(2)Fe14B/Fe3B nanocomposite ribbons have been synthesized by melt spinning of Nd3Tb1Fe76Cu0.5Nb1B18.5 alloys. Tb substitution has significantly enhanced the value of coercivity and Curie temperature. Highest value of coercivity has been obtained as 4.76 kOe for the sample annealed at 953 K for 10 min. Curie temperature of Tb substituted sample, Nd3Tb1Fe76Cu0.5Nb1B18.5 is 549 K while Curie temperature of the sample without Tb, Nd4Fe76Cu0.5Nb1B18.5 is 535 K. Recoil hysteresis loops measured along the major demagnetization curve are steep having small recoil loop area. Temperature dependence of coercivity, remanent ratio and maximum energy product have been measured for the sample annealed at 893 K and 923 K for 10 min. At 5 K, coercivity and maximum energy product of the sample annealed at 893 K for 10 min are 5.2 kOe and 11.5 MGOe respectively and the sample annealed at 923 K for 10 min are 6 kOe and 13.1 MGOe respectively.
| Item Type: | Article |
|---|---|
| Subjects: | Physical Science > Nanophysics Physical Science > Nano objects Material Science > Nanochemistry Material Science > Nanostructured materials |
| Divisions: | Faculty of Engineering, Science and Mathematics > School of Physics Faculty of Engineering, Science and Mathematics > School of Chemistry |
| ID Code: | 9813 |
| Deposited By: | JNCASR |
| Deposited On: | 10 Nov 2010 05:10 |
| Last Modified: | 10 Nov 2010 05:10 |
Repository Staff Only: item control page