Effects of ultrasound in coating nano-precipitated CaCO3 with stearic acid

Kow, K. W. and Abdullah, E.C. and Aziz, A.R. (2009) Effects of ultrasound in coating nano-precipitated CaCO3 with stearic acid. ASIA-PACIFIC JOURNAL OF CHEMICAL ENGINEERING , 4 . pp. 807-813. ISSN 1932-2143

Full text is not hosted in this archive but may be available via the Official URL, or by requesting a copy from the corresponding author.

Abstract

Nano-Precipitated CaCO3 (NPCC) are coated with stearic acid to improve its dispersion in polymer as well as to reduce agglomeration. In this work, coating was done by wet method using ethanol. Ultrasonication was applied to NPCC to de-agglomerate micron size NPCC into smaller size. Effects of amplitude, temperature and energy input of ultrasonication was investigated. The amplitude was varied from 60% to 100% whereas temperature was varied from 5 degrees C to 45 degrees C. The energy input was stressed up from 3.6 kJ to 180 kJ. Mean diameter of NPCC were observed by using Particle Size Analyzer and Transmission Electron Microscopy (TEM). It was found that mean diameter of NPCC do not vary significantly with temperature. Mean diameter of NPCC, however, decreases exponentially with the energy input. Comparisons were done on NPCC coated with others methods such as dry ball milling and aqueous coating TEM images show that coating NPCC with ultrasonication is more uniform than other methods. In addition, first derivative mass loss with temperature (DTG) reveals that NPCC coated with Ultrasonication do not contain excessive free acid as exhibited by those coated in aqueous and dry ball milling.

Item Type:Article
Subjects:Material Science > Nanochemistry
Material Science > Nanostructured materials
ID Code:7862
Deposited By:CSMNT
Deposited On:27 Nov 2009 16:43
Last Modified:27 Nov 2009 16:43

Repository Staff Only: item control page