Lu, Da-Yong (2009) Influence of dc bias field on dielectric properties of high-k Y5V (Ba, La)(Ti, Ce)O3 ceramic. Materials Letters, 63 (20). 1722 - 1724.
Full text is not hosted in this archive but may be available via the Official URL, or by requesting a copy from the corresponding author.
Official URL: http://www.sciencedirect.com/science/article/B6TX9...
Abstract
The influence of dc bias field (Ebias) on the dielectric properties of high-k Y5V (Ba0.97La0.03)(Ti0.94Ce0.05)O3 ceramic (BL3TC5) was investigated. With increasing Ebias from 1 to 12.5 kV/cm, dielectric permittivity and dielectric loss were suppressed, and the permittivity maximum decreased linearly. Upon field heating and field cooling, the temperature of the permittivity maximum shifted to higher temperatures; however, the dielectric heat relaxation decreased with increasing Ebias. As Ebias ≥ 10 kV/cm, the frequency dispersion vanishes. The model of polar nano-domains is proposed to account for dielectric behavior under dc bias field. In addition, BL3TC5 shows high tunability (~ 67%) and low loss (< 0.008) at room temperature.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Barium lanthanum titanate cerate; Ceramics; Perovskite relaxor; Bias; Dielectrics; Tunability |
| Subjects: | Material Science > Nanostructured materials |
| ID Code: | 6578 |
| Deposited By: | SPI |
| Deposited On: | 10 Feb 2010 17:33 |
| Last Modified: | 10 Feb 2010 17:33 |
Repository Staff Only: item control page