Yu, Ya-Wen and Cho, Chun-Pei and Perng, Tsong-Pyng (2009) Crystalline Gaq3 Nanostructures: Preparation, Thermal Property and Spectroscopy Characterization. Nanoscale Research Letters, 4 (8). pp. 820-827.
Official URL: http://www.springerlink.com/content/0l76h273077n14...
Crystalline Gaq3 1-D nanostructures and nanospheres could be fabricated by thermal evaporation under cold trap. The influences of the key process parameters on formation of the nanostructures were also investigated. It has been demonstrated that the morphology and dimension of the nanostructures were mainly controlled by working temperature and working pressure. One-dimensional nanostructures were fabricated at a lower working temperature, whereas nanospheres were formed at a higher working temperature. Larger nanospheres could be obtained when a higher working pressure was applied. The XRD, FTIR, and NMR analyses evidenced that the nanostructures mainly consisted of Î´-phase Gaq3. Their DSC trace revealed two small exothermic peaks in addition to the melting endotherm. The one in lower temperature region was ascribed to a transition from Î´ to Î² phase, while another in higher temperature region could be identified as a transition from Î² to Î´ phase. All the crystalline nanostructures show similar PL spectra due to absence of quantum confinement effect. They also exhibited a spectral blue shift because of a looser interligand spacing and reduced orbital overlap in their Î´-phase molecular structures.
|Uncontrolled Keywords:||Gaq3 - 1-D nanostructures - Nanospheres - Thermal evaporation - Crystallization - Phase transition|
|Subjects:||Material Science > Nanofabrication processes and tools|
Material Science > Nanostructured materials