Thermal stability of nanostructurally stabilized zirconium oxide

Namavar, Fereydoon and Wang, Gonghua and Cheung, Chin Li and Sabirianov, Renat F. and Zeng, Xiao Cheng and Mei, Wai Ning and Bai, Jaeil and Brewer, Joseph R. and Haider, Hani and Garvin, Kevin L. (2007) Thermal stability of nanostructurally stabilized zirconium oxide. NANOTECHNOLOGY, 18 (41).

Full text is not hosted in this archive but may be available via the Official URL, or by requesting a copy from the corresponding author.

Official URL: http://www.iop.org/EJ/abstract/0957-4484/18/41/415...

Abstract

Nanostructurally stabilized zirconium oxide ( NSZ) hard transparent films were produced without chemical stabilizers by the ion beam assisted deposition technique ( IBAD). A transmission electron microscopy study of the samples produced below 150 degrees C revealed that these films are composed of zirconium oxide ( ZrO2) nanocrystallites of diameters 7.5 +/- 2.3 nm. X- ray and selected- area electron diffraction studies suggested that the as- deposited films are consistent with cubic phase ZrO2. Rutherford backscattering spectroscopy ( RBS) indicated the formation of stoichiometric ZrO2. The phase identity of these optically transparent NSZ films was in agreement with cubic ZrO2, as indicated by the matching elastic modulus values from the calculated results for pure cubic zirconium oxide and results of nanoindentation measurements. Upon annealing in air for 1 h, these NSZ films were found to retain most of their room temperature deposited cubic phase x- ray diffraction signature up to 850 degrees C. Size effect and vacancy stabilization mechanisms and the IBAD technique are discussed to explain the present results.

Item Type:Article
Uncontrolled Keywords:ZRO2 THIN-FILMS; BARRIER COATINGS; PHASE; PERFORMANCE; MECHANISMS; DEPOSITION
Subjects:Analytical Science > Microscopy and probe methods
Material Science > Functional and hybrid materials
ID Code:6343
Deposited By:IoN
Deposited On:28 Sep 2009 12:24
Last Modified:28 Sep 2009 12:24

Repository Staff Only: item control page