Krishnaswamy, Rama and Majumdar, Sayantan and Ganapathy, Rajesh and Agrawal, Ved Varun and Sood, A. K. and Rao, C. N. R. (2007) Interfacial Rheology of an Ultrathin Nanocrystalline Film Formed at the Liquid/Liquid Interface. Langmuir, 23 (6). pp. 3084-3087.
Full text is not hosted in this archive but may be available via the Official URL, or by requesting a copy from the corresponding author.
We report the interfacial properties of monolayers of Ag nanoparticles 10−50 nm in diameter formed at the toluene−water interface under steady as well as oscillatory shear. Strain amplitude sweep measurements carried out on the film reveal a shear thickening peak in the loss moduli (G‘ ‘) at large amplitudes followed by a power law decay of the storage (G‘) and loss moduli with exponents in the ratio 2:1. In the frequency sweep measurements at low frequencies, the storage modulus remains nearly independent of the angular frequency, whereas G‘ ‘ reveals a power law dependence with a negative slope, a behavior reminiscent of soft glassy systems. Under steady shear, a finite yield stress is observed in the limit of shear rate γ̇ going to zero. However, for γ̇ > 1 s-1, the shear stress increases gradually. In addition, a significant deviation from the Cox−Merz rule confirms that the monolayer of Ag nanoparticles at the toluene−water interface forms a soft two-dimensional colloidal glass.
|Subjects:||Material Science > Nanochemistry|
|Divisions:||Faculty of Engineering, Science and Mathematics > School of Physics|
Faculty of Engineering, Science and Mathematics > School of Chemistry
|Deposited On:||20 Jan 2009 10:04|
|Last Modified:||03 Apr 2009 13:02|
Repository Staff Only: item control page